Low Smoke Halogen Free & High Flame Retardant Cable Sheathing Compound

Price: US $ 1 - 5 / Kilogram
Brand Name: KINGFISHER
Model Number: HFFR9008
Country/Region: China
Post Date: Mar 17,2012

Product Description: Low Smoke Halogen Free & High Flame Retardant Cable Sheathing Compound


Application:   

1.Coat layer for metro,

2.mine

3.electric power and ships

 

Specifications:

(a) Halogen-free & low smoke cable sheathing compound 
(b) High flame retardant property 
(c) Less toxicity 
(d) Smooth surface 

 

Brief Introduction:

1.These granules are produced base on polyolefin added with different halogen-free additive and special mix granulated process. The final jacking compound release less smoke, no halogen and low toxicity when burning also with good flame retardant properties and great processing ability. The cable extruded has smooth surface which properties can be compared with the similar products abroad.  

Processing:                                                                     

2.These granules can be extruded by general single screw extrusion machine. The specific extrusion speed and temperature should be adjusted according to different equipments.

 

Suggested screws:

1.Compression ratio, better between 2.1-2.3, 

2.Length-to-diameter ratio  ≥1:20.

 

Suggested processing temperature: 

1.Zone 1: 105°C ,

2.Zone 2: 115°C , 

3.zone 3: 125°C ,

4.Zone 4: 130°C , 

5.Zone 5: 135°C, 

6.Head Zone: 135°C.

 

Packaging:

Kraft paper bag outside inside Vacuum-packed with aluminum foil 25KG/bag. 

 

Properties

 

NO.

Item

Unit

Test Method

Technical Requirement

Test Result

1

Original Tensile Strength

Mpa

GB/T 2951.11-2008

≥9.0

12.7

2

Original Elongation at Break

%

GB/T 2951.11-2008

≥150

170

3

After Hot air aging(100°C, 168h)

 

GB/T 2951.12

 

 

3.1

Tensile Strength

Mpa

GB/T 2951.11-2008

≥9.0

13.1

3.2

Variation of Tensile Strength

%

GB/T 2951.11-2008

Within ±30

3.2

3.3

Elongation at Break

%

GB/T 2951.11-2008

≥120

150

3.4

Variation of Elongation at Break

%

GB/T 2951.11-2008

Within ±30

-12

4

Thermal Deformation(90°C, 4h)

%

GB/T 2951.31-2008

≤50

15

5

Impact Brittleness(-25°C)-           Brittle Failure

 

GB/T 2951.14

≤15/30

0/30

6

Volume Resistivity at 20°C

Ω.cm

GB/T 1410-2006

≥1.0x1010

1.8x1013

7

Dielectric Strength

MV/m

GB/T 2951.51-2008

≥18

31

8

Smoke Density

 

GB/T 8323.1 GB/T 8323.2

 

 

8.1

flame

 

/

≤250

219

8.2

no flame

 

/

≤100

75

9

Oxygen Index

%

GB/T 2406.1

≥32

35.6

10

Acid gas Content

mg/g

GB/T 17650.1

≤5

0

11

PH

 

GB/T 17650.2

≥4.3

5.7

12

Conductivity

μs/mm

GB/T 17650.2

≤10

0.46

13

Toxicity Index

 

GB/T 17650.1

≤5

1.8

14

Density

g/cm3

GB/T 2951.13-2008

≤1.46

1.43

 The above information is given based on our present state of knowledge,As there are numerous variation in industrial practice, the information as given is without obligation and liability of whatever on our part.

 

 

 

Supplier Details:

Wuxi Changhong Masterbatches Co., Ltd.

Sales:Mr. Xu Yunlong

Contact Phone:86-510-83958699

Main Products:Black Masterbatch, White Masterbatch, Color Masterbatch, Additive Masterbatc

SPONSOR AD

User Reviews: Low Smoke Halogen Free & High Flame Retardant Cable Sheathing Compound